美国高温合金:
405 406 409 430 434 439 18SR 18Cr-2Mo 446 E-Brite26-1 26-1Ti 29Cr-4Mo 403 410 416 422 H-46 MolyAscoloy GreekAscoloy JetheteM-152 Almar363 431 Custom450 Custom455 15-5PH 17-4PH PH13-8Mo AM-350 S40500 S40900 S43000 S43400 S43927 S44600 S44627 S40300 S41000 S41600 S42200 S43100 S15500 S17400 S13800 S35000 AM-355 17-7PH PH15-7Mo 304 304L 304N 309 310 316 316L 316N 317 321 347 19-9DL 17-14-CuMo 202 216 21-6-9 Nitronic32 Nitronic33 Nitronic60 Carpenter18-18Plus S35500 S17700 S15700 S30400 S30403 S30451 S30900 S31000 S31600 S31603 S31651 S31700 S32100 S34700 K63198 K63199 S20200 S21600 S21900 16-25-6 17-14CuMo 19-9DL Carpenter20Cb-3 Incoloy800 Incoloy801 Incoloy802 N-155 RA330 Haynes25(L-605) Haynes188 S-816 Stellite6B UMCo-50 HastelloyB HastelloyB-2 HastelloyC HastelloyC-4 HastelloyC-276 HastelloyN HastelloyS HastelloyW HastelloyX Incone1600 Incone1601 Incone1604 Incone1617 Incone1625 NA-224 Nimonie75 RA-333 A-286 Discaloy Haynes556 Incoloy903 PyrometCTX-1 K63198 N08020 N0800 N08801 R30155 N08330 R30605 R30188 R30816 N10001 N10065 N10002 N06455 N10276 N10003 N10004 N06002 N06600 N06601 N06625 N06333 K66286 K66220 V-57 W-545 AR-213 MP-35N MP-159 Astroloy D-979 IN100 IN102 Incoloy901 Incoloy1706 Incoloy1718 Incoloy1751 IncoloyIX750 M252 Nimonic80A Nimonic90 Nimonic95 Nimonic100 Nimonic105 Nimonic115 Nimonic263 Pyromet860 Refractory26 Rene4L Rene95 Rene100 Udimet500 Udimet520 Udimet630 Udimet700 Udimet710 UnitempAF2-1DA Waspaloy K66545 R30035 N09979 K66979 N13100 N06102 N09901 N09706 N07718 N07750 N07252 N07080 N07090 N07041 N07500 N07001 HA HC HD HE HF HH HI HK HLHN HP HP-50WZ HT HU HW HX J92605 J93005 J93403 J92603 J93503 J94003 J94224 J94604 J94213 J94605 A217 A297 A608 A567 A351 B-1900 HastelloyX IN-100 IN-738X IN-792 Inconel713C Inconel713LC Inconel718 InconelX-750 M-252 MAR-M200 MAR-M246 MAR-M247 NX188(DS) Rene77 Rene80 Rene100 TRWNASIA Udimet500 Udimet700 Udimet710 Waspaloy WAZ-20(DS) AiResist13 AiResist213 AiResist215 Haynes21 Haynes25,L-605 Haynes151 J-1650 MAR-M302 MAR-M322 MAR-M509 MAR-M918 NASACo-W-Re S-816 V-36 WI-52 X-40
英国高温合金:
N75 N80A N90 N105 N115 N118 N901 N263 NimonicPE11 NimonicPE16 NimonicPK33 EPK57 PE13 C130 C242 C1023 NimocastPE10 NimocastPD16 NimocastPD18 NimocastPK24 Stellite31 MM002 Haynes25
法国高温合金:
ATVSMo ATVS2 ATVS7 ATVS7Mo ATGC1 ATGE ATGE2 ATGF ATGM2 ATGR ATGS3 ATGS4 ATGS8 ATGS9 ATGW0 ATGW1 ATGW2 ATGW3 ATGW4 ATGX ATGXX ATG33 ARC1628 ARC6015 NCRALZ NCRALC NCRALK25 KCN22W NW12KCATHf NC15K10DAT KC25NW 28NCD Z6NCT25 Z3NCT25-Z4CDT26 Z10NKC30 Z6NKCDT.38 NC19FeNb NC22FeD NC22FeD NC22FeDNb NC15TNbA KC20WN NK15CAT NC20T NC20TA NC20KTA NK27CADT NC13AD NCK20D NC20K14 NC20KDTA NK18CDAT NCK18TDA Z12CNKDW20 Z42CKNDW20 Z6NCKDW45 ND27FeV NC17DWY NC15Fe 25NC3520 NC21FeDU KCN22W NW12KCATHf NC15K10DAT KC25NW Z8NCD
德国高温合金:
NiMo16Cr NiCr22Mo NiCr21Fe18Mo NiCr20Mo15 NiMo16Cr16Ti S-NiMo16Cr16Ti S-NiMo15Cr15 S-NiCr21Fe18Mo S-NiMo27 S-NiMo29 NiMo28 NiCr22Mo6Cu NiCr22Mo7Cu S-NiCr16FeMn NiCr20Ti NiCr20TiAl NiCr20Co18Ti NiCo20Cr15MoAlTi NiCo15Cr15MoAlTi S-NiCr20 NiCr15Fe NiCr21Mo5Cu NiCo20Cr20MoTi S-NiCr20Mo9 S-NiCr28Mo S-NiCr27Mo S-NiCr29Mo S-NiCr19Mo15 NiCr30 NiCr20CuMo NiCr23Co12Mo NiCr23Co12Mo NiCr19NbMo NiCr15Fe7TiAl GNiCr50Nb NiCr16TiAl S-NiMo28 S-NiCr15FeTi S-NiCr15FeNb S-NiCr20Nb S-NiCr15FeMn S-NiCr20 NiMo30 NiCr20Mo15 G-NiCr50Nb NiCr15Fe NiMo16Cr15W S-NiCr20Mo15 G-X40NiCrSiNb3818 X15NiCrNb3221 NiCr23Fe G-X40NiCrSiNb3525 X40NiCrNb3525 G-X30CrNiSiNb2424 NiCr22Mo9Nb GX40NiCrSi3525 NiCr21Mo G-X10NiCrNb3220 NiCr3020 X10NiCr3220 X12NiCr3618 X12NiCrSi3616 G-X40NiCrSi3818 NiCr6015,NiFe20Cr15 G-X50CrNi3030 NiCr8020,NiCr20 NiCr10 X10NiCrAlTi3220 G-NiCr28W S-NiCr28W G-NiMo30 G-NiMo16Cr S-NiMo16Cr16W S-NiMo15Cr15W NiCr20Ti NiCr20TiAl NiFe25Cr20NbTi X7CrNiCo212020 G-X15CrNiCo212020 X40CrNiCoNb1313 CoCr20W15Ni CoCr20W15Ni GX7CrNiNb1613 NiCr20Co18Ti X12CrCoNi2120 NiCr19CoMo NiFeCr12Mo NiCr20Mo X40CoCrNi2020 X50CoCrNi2020 CoCr28MoNi X5NiCrTi2615 X8CrNiMoNb1616 NiCr20CbMo NiCr18Co CoCr20Ni20W 2.4602 2.4603 2.4605 2.4606 2.4607 2.4610 2.4611 2.4612 2.4613 2.4615 2.4616 2.4617 2.4618 2.4619 2.4620 2.4630 2.4631 2.4632 2.4634 2.4636 2.4639 2.4640 2.4641 2.4650 2.4651 2.4653 2.4654 2.4655 2.4656 2.4657 2.4658 2.4660 2.4662 2.4663 2.4665 2.4666 2.4668 2.4669 2.4670 2.4676 2.4680 2.4685 2.4686 2.4890 2.4802 2.4803 2.4805 2.4806 2.4807 2.4508 2.4810 2.4811 2.4813 2.4816 2.4819 2.4839 2.4849 2.4850 2.4851 2.4852 2.4853 2.4855 2.4856 2.4857 2.4858 2.4859 2.4860 2.4861 2.4863 2.4864 2.4865 2.4867 1.4868 2.4869 2.4870 1.4876 2.4879 2.4882 2.4883 2.4886 2.4887 2.4951 2.4952 1.4954 2.4955 1.4956 1.4957 1.4960 2.4964 2.4967 1.4968 2.4969 1.4971 2.4973 1.4974 2.4975 2.4976 1.4977 1.4978 1.4979 1.4980 1.4981 2.4982 2.4983 2.4989
日本高温合金:
NCF600 NCF601 NCF750 NCF751 NCF800 NCF800H NCF825 NCF80A NCF1B NCF3 NCF2B
秉争实业有限公司追求与客户长期、稳定、互动的合作关系，努力当好 河池精密合金与用户沟通的纽带。公司以优惠的 河池精密合金出厂价，优质的商家服务愿与广大新老客户携手共进，共同发展。企业目标: 以优质的服务满足广大客户的需求，以质优价廉 的 河池精密合金取得广大客户的信任。不断发展，做行业的领跑者。企业文化：广交朋友，合作共赢。
沉淀硬化钢常用牌号：
17-4PH/0Cr17Ni4Cu4Nb/05Cr17Ni4Cu4Nb/AISI630,UNS S17400/SUS630/X5CrNiCuNb16-4/PH15-7Mo/（UNS S15700、SUS 632）0Cr15Ni7Mo2Al/ AM-350(UNS S35000/SUS 633)0Cr16Ni4Mo3N/17-7PH(SUS 631) 07Cr17Ni7Al/UNS S17700/AISI 631/ PH13-8Mo/0Cr13Ni8Mo2Al（UNS S13800、XM13/04Cr13Ni8Mo2Al/15-5PH（UNS S15500、XM12）1.4545/XM-12/05Cr15Ni5Cu4Nb/0Cr15Ni5Cu4Nb/Custom-455/00Cr12Ni8Cu2TiNb /AM-355(634型) AM350/0Cr16Ni4Mo3N
沉淀硬化型钢为马氏体型沉淀硬化不锈钢，有较高的强度、耐蚀性、抗氧化性，热加工性能良好，可加工性与同等硬度的马氏体型不锈钢相似。在固溶、时效状态下，可用不锈钢的焊接方法进行焊接。
热处理规范
(1)固溶1020～1060℃快冷;
(2)480℃时效,经固溶处理后,470～490℃空冷;
(3)550℃时效,经固溶处理后,540～560℃空冷;
(4)580℃时效,经固溶处理后,570～590℃空冷;
(5)620℃时效,经固溶处理后,610～630℃空冷。
用途
用于制造在400℃以下工作的高强度耐蚀件，如飞机中的重要螺栓、销等紧固件、发动机零件及阀门、＊＊＊＊具等添加铜的沉淀硬化型钢种。用于制造轴类、汽轮机部件。广泛用于航空、石油、化工、纺织、食品、医疗器械等部门要求耐腐蚀性能的容器、构件、工具和零件等
1、GH4169高温合金
GH4169合金是镍一铬一铁基高温合金。GH4169合金属于镍基变形高温合金。镍基合金是一种最复杂的合金。它被广泛地应用于制造各种高温部件。同时，也是所有高温合金中最为注目的一种合金。它的相对使用温度在所有普通合金系中也是最高的。目前，先进的飞机发动机中这种合金的比重在50%以上。
GH4169合金是由国际镍公司亨廷顿分公司的Eiselstein研制成功，于1995年公开介绍的时效硬化镍—铬—铁基变形合金。合金是以体心立方g〞和面心立方g′相为沉淀强化的一种镍基变形高温合金，在650℃以下具有高的抗拉强度、屈服强度和良好的塑性，具有良好的抗腐蚀、抗辐射能、疲劳、断裂韧性等综合性能，以及满意的焊接和焊后成型性能等。合金在-253～650℃很宽的温度范围内组织性能稳定，成为在深冷和高温条件下用途极广的高温合金。由于GH4169良好的综合性能，目前被广泛用于航空发动机的压气机盘、压气机轴、压气机叶片、涡 、涡轮轴、机匣、紧固件和其它结构件和板材焊接件等 [3] 。
我国于70年代开始研制GH4169合金，主要应用于盘件，使用时间比较短，所以采用真空感应加电渣重熔的双联工艺。八十年代开始应用于航空领域，提高和改进材料质量、提高合金的综合性能和使用可靠性成为主要的研究方向。当前GH4169合金的主要研究方向为：
（1）改进冶炼工艺，量化冶炼参数，实现程序稳定操作，使合金显组织更加均匀，从而得到优良的屈服和疲劳强度以及抗裂纹扩展止裂能力，提高低周疲劳强度等；
（2）改进热处理工艺。目前的热处理工艺不能很好的消除钢锭中心的偏析，所以对组织的均匀性有不利影响，因此采用合理的均匀化退火工艺，得到细晶坯料成为现在的主要研究方向之一；
（3）改进使用设计。由于GH4169的工作温度不能高于650℃，所以应当加强零部件的冷却，充分发挥该高温合金的高性能、低成本等优点；
（4）提高组织稳定性能。由于航空发动机部件的长寿命要求，对于提高GH4169合金长期时效组织稳定性方面也是至关重要的。
2、单晶高温合金
目前单晶合金材料已发展到第四代，承温能力提升到1140℃，已近金属材料使用温度极限。未来要进一步满足先进航空发动机的需求，叶片的研制材料要进一步拓展，陶瓷基复合材料有望取代单晶高温合金满足热端部件在更高温度环境下的使用。
单晶高温合金叶片研制难度和周期与其结构复杂性有关，普通复杂程度的单晶叶片研制周期较短，但在航空发动机上应用也需经历较长的时间。从单晶实心叶片到单晶空心叶片、到高效气冷复杂空心叶片等，技术难度跨度很大，相应的研制周期跨度也较大。一般一种普通复杂程度的单晶空心叶片从图纸确认、模具设计到试制、再到小批投产，需要1～2年时间。但单晶叶片由于其复杂的服役环境，需要进行大量的验证试验，一般一种普通结构的单晶空心叶片从研制出来以后到航空发动机上应用需5～10年的时间，有的随发动机研制进度，甚至需要15年或更长的时间 [4] 。